Growth of superconducting boron doped diamond on 4inch silicon wafers

RESUMO

Superconducting boron-doped diamond (BDD) films were grown on 4-inch silicon wafers by microwave plasma chemical vapour deposition using gas-phase B/C ratios ranging from 6536 to 36421 ppm. Surface morphology, boron incorporation and superconducting properties were investigated as a function of gas-phase boron concentration. No systematic variation in apparent lateral grain size was observed across the series. Superconductivity was observed in all films except that grown at a B/C ratio of 6536 ppm within the measured temperature range down to 2 K. The superconducting transition temperature initially increased with increasing B/C ratio, reaching a maximum T$_c$ of 4.03 K at 24691 ppm, before decreasing at higher gas-phase B/C ratios. The corresponding resistive upper critical field at 2 K reached 3.091 T. Raman spectroscopy showed an increase in boron incorporation with increasing gas-phase B/C ratio up to 30303 ppm, followed by a slight decrease at 36421 ppm. Spatial measurements across the film grown at 24691 ppm showed T$_c$ values of 4.02, 4.19 and 3.33 K at the centre, intermediate and edge positions, respectively, with Raman spectroscopy showing a corresponding spatial variation in boron concentration. Comparison with previous growth on 2-inch wafers showed that substantially higher gas-phase B/C ratios were required to obtain comparable boron concentrations and superconducting properties on 4-inch wafers, indicating reduced boron incorporation efficiency during large-area growth. These results demonstrate the feasibility of producing superconducting BDD over a substantial area of a 4-inch silicon wafer while identifying boron incorporation and radial uniformity as key parameters for further wafer-scale optimisation.