Phonon-Bottleneck-Governed Ultrafast Hot-Carrier Super-Diffusion in Transition Metal Dichalcogenides

RESUMO

Two-dimensional transition metal dichalcogenides (TMDCs) are promising for low-power optoelectronics, yet their operational speed is widely considered constrained by low room-temperature mobilities and carrier transit delays. Here, by combining on-chip terahertz optoelectronic sampling with thermally evaporated Ohmic contacts, we eliminate external parasitic delays and directly capture the intrinsic interfacial photoresponse in unencapsulated TMDCs under zero bias. The devices achieve ultrafast relaxation lifetimes of 48.5 ps in MoS2/Au and 14.2 ps in MoSe2/Ag, translating to intrinsic 3-dB bandwidths of 4.4 GHz and 7.5 GHz, respectively. Spatial scanning and bias-dependent measurements show that this response is position-independent and bias-immune, ruling out conventional drift-limited transport and identifying hot-carrier super-diffusion driven by an interfacial electron temperature gradient as the operative mechanism. Furthermore, ultrafast pump-probe spectroscopy reveals that the macroscopic response time is quantitatively synchronized with the microscopic optical-to-acoustic phonon scattering lifetime governed by the intrinsic phonon bottleneck. Our findings establish phonon engineering as a viable paradigm to tailor non-equilibrium optoelectronic dynamics, offering a blueprint for zero-bias, ultrafast, self-powered devices.